Modified Shrinking Core Model for Atomic Layer Deposition of TiO2 on Porous Alumina with Ultrahigh Aspect Ratio

作者：Park Inhye; Leem Jina; Lee Hoo Yong; Min Yo Sep^*

来源：BULLETIN OF THE KOREAN CHEMICAL SOCIETY, 2013, 34(2): 519-523.

DOI：10.5012/bkcs.2013.34.2.519

• Shrinking core model
• Atomic layer deposition
• TiO2
• Porous alumina
• Aspect ratio

When atomic layer deposition (ALD) is performed on a porous material by using an organometallic precursor, minimum exposure time of the precursor for complete coverage becomes much longer since the ALD is limited by Knudsen diffusion in the pores. In the previous report by Min etal. (Ref. 23), shrinking core model (SCM) was proposed to predict the minimum exposure time of diethylzinc for ZnO ALD on a porous cylindrical alumina monolith. According to the SCM, the minimum exposure time of the precursor is influenced by volumetric density of adsorption sites, effective diffusion coefficient, precursor concentration in gas phase and size of the porous monolith. Here we modify the SCM in order to consider undesirable adsorption of byproduct molecules. TiO2 ALD was performed on the cylindrical alumina monolith by using titanium tetrachloride (TiCl4) and water. We observed that the byproduct (i.e., HCl) of TiO2 ALD can chemically adsorb on adsorption sites, unlike the behavior of the byproduct (i.e., ethane) of ZnO ALD. Consequently, the minimum exposure time of TiCl4 (similar to 16 min) was significantly much shorter than that (similar to 71 min) of DEZ. The predicted minimum exposure time by the modified SCM well agrees with the observed time. In addition, the modified SCM gives an effective diffusion coefficient of TiCl4 of similar to 1.78 x 10(-2) cm(2)/s in the porous alumina monolith.

• 出版日期2013-2-20