NixCo1-x alloy nanoparticle-doped carbon nanofibers as effective non-precious catalyst for ethanol oxidation

作者：Barakat Nasser A M^*; Motlak Moaaed; Elzatahry Ahmed A; Khalil Khalil Abdelrazek; Abdelghani Emad A M

来源：International Journal of Hydrogen Energy, 2014, 39(1): 305-316.

DOI：10.1016/j.ijhydene.2013.10.061

• Direct ethanol fuel cells
• Electrospinning
• Nanofibers
• Nickel alloys
• Carbon nanofibers

Alloy structure generates special characteristics for the nano-metallic compounds which make this interesting class of materials promising candidates for many application fields. Moreover, the performance of the nanostructural catalysts is strongly influenced by the morphology; nanofibers reveal distinct catalytic activity compared to the nanoparticles. In this study, non-precious electrocatalysts based on alloy structure and nanofibrous morphology are introduced. Briefly, NixCo1-x (x = 0.0, 0.1, 0.3, 0.5, 0.7, 0.9 and 1.0) alloy nanoparticles incorporated in carbon nanofibers are investigated as electrocatalysts for ethanol oxidation. Preparation of the introduced nanofibers could be achieved by calcination of electrospun nanofibers composed of nickel acetate tetrahydrate, cobalt acetate tetrahydrate and poly(vinyl alcohol) in argon atmosphere at 800 degrees C. Polycondensation characteristic of the utilized metals precursors led to produce good morphology electrospun nanofibers as well as preserved the nanofibrous morphology during the calcination process for all formulations. The catalytic activity of cobalt enhanced the carbonization of the utilized polymer which resulted in producing nickel/cobalt alloys nanoparticles embedded in carbon nanofibers. Electrochemical investigation of the introduced nanofibers toward ethanol oxidation indicated that the alloy structure has a strong influence. For instance, the corresponding current densities of Ni- and Ni0.9Co0.1-doped carbon nanofibers were 37 and 142 mA/cm(2), respectively. Moreover, very low onset potential (-50 mV vs. Ag/AgCl) was observed when Ni0.1Co0.9-doped carbon nanofibers were utilized. Furthermore, Ni0.9Co0.1-doped carbon nanofibers could oxidize ethanol solution up to 5 M due to the observed active layer regeneration. The introduced nanofibers have good stability because of the alloy structure. Overall, this study opens new avenue for the transition metals alloys and the nanofibrous morphology to produce novel and effective non-precious electrocatalysts.

• 出版日期2014-1-2