In this study, the physicochemical properties of several commercial ultrafine TiO2 powders and their behaviour in the as-received form and colloidal suspensions were analysed. Besides the particle size, the morphology and agglomeration state of the dry powders, dispersibility, zeta-potential and sedimentation in water and in phosphate-buffered saline (PBS) were studied. Also, leaching of ions from the powders during ageing in physiological solution and the ability of the photoactivated powders to decompose organic substances were evaluated. The examined TiO2 powders revealed diversified characteristics when dispersed in water. In general, while in dry conditions the particle size appeared in the nano-range (down to 32 nm), the particles were agglomerated in aqueous suspensions at pH similar to 7 and only a minor amount showed dimensions below 200 nm, but none below 100 nm. The inherent pH of the 3 % suspensions varies from 3.7 to 7.5 and the surface charge at these pH values varied from highly positive to highly negative values. In PBS, the surface charge is negative and relatively low for all the samples, which resulted in agglomeration. Five out of six powders exhibited significant photocatalytic activity when exposed to UV irradiation. This also includes one cosmetic-grade powder. Furthermore, during the immersion in aqueous media at physiological temperature, the powders released foreign ions, which might also contribute to the results of cytotoxicity tests. The results revealed the major role of the particle surface charge and its impact on particle dispersion or agglomeration. Due to the high ionic strength in the liquids relevant for cell-surface interaction tests, for all the examined titania powders the nanoparticulate character was lost. However, the presence of impurities and photocatalysis might further contribute to the results of cytotoxicity tests.
- 出版日期2016-5-12