Determination of environmental stress cracking resistance of polymers: Effects of loading history and testing configuration

作者：Andena Luca^*; Castellani Leonardo; Castiglioni Andrea; Mendogni Andrea; Rink Marta; Sacchetti Francisco

来源：Engineering Fracture Mechanics, 2013, 101: 33-46.

DOI：10.1016/j.engfracmech.2012.09.004

• Polymers
• Fracture mechanics
• Environmental cracking
• Life prediction

Industry requires methods able to quickly characterize the environmental stress cracking (ESC) resistance of polymeric materials for R and D and quality control purposes. None of the available standards is completely satisfactory and their reliability is often not sufficient. In this paper the fracture mechanics (FM) approach has been successfully applied to characterize the ESC behaviour of two different high-impact polystyrene grades. Data in air were compared with those in an active environment (sunflower oil), adopting different test configurations (double cantilever beam, four point bending and buckled plate) under different loading histories (respectively constant displacement rate, creep and relaxation). A strong effect of the active environment was observed but only above a characteristic interaction time. FM parameters proved to be independent from the applied loading history/configuration, thus allowing ranking of different materials and components' lifetime predictions.

• 出版日期2013-3