Mechanical and thermal properties improvement of unsaturated polyester resin by incorporation of TiO2 nanoparticle surface modified with titanate

作者：Jiang, Chaohua; Jin, Chen; Wei, Min; Yan, Sheng; Chen, Da^*

来源：Materials Research Express, 2018, 5(11): 115008.

DOI：10.1088/2053-1591/aadc42

• nanocomposites
• unsaturated polyester resin
• TiO2 nanoparticle
• mechanical properties
• thermal properties

Unsaturated polyester resin (UPR)/titanium dioxide (TiO2) nanocomposites were obtained by the incorporation of TiO2 nanoparticle surface modified with titanate in the UPR. The mechanical properties, thermal behavior, anti-ultraviolet aging properties and composite microstructure were tested. The results show that TiO2 nanoparticles have a good compatibility with the UPR matrix. When the contents of TiO2 and titanate coupling agent are 4% and 3% respectively, the impact strength, flexural strength and heat deflection temperature of the composites are 16.28 kJm(-2), 63.23 MPa, and 70.3 degrees C, respectively, which increase by 890.5%, 77.5% and 23.7% compared with pure UPR. The incorporation of modified TiO2 nanoparticles in the UPR enhances the anti-ultraviolet aging properties of the composites. When 4% TiO2 nanoparticles are added to the UPR, the impact strength retention rate improves by 29.8% compared with pure UPR at 60 days. Strengthening and toughening effects with the incorporation of TiO2 can be achieved by forming a flexible interface layer between the TiO2 and UPR matrix because of the higher rigidity, excellent bonding and compatibility of the TiO2.

• 出版日期2018-11
• 单位河海大学; 南京工业大学