Mg-8Li-3Al-0.7Si alloy was prepared by casting and deformed by hot extrusion in this study. And the microstructure of as-cast and extruded specimens was analyzed with OM, XRD, SEM and EDS. Results show that the specimens are composed of alpha-Mg, beta-Li, AlLi, MgLiAl2 and Mg2Si phases. In as-extruded specimen, the microstructure is refined and the beta-Li phase has the effect of coordination during deformation. After hot extrusion, Chinese script Mg2Si phase is crushed into block-like and distributes uniformly in the matrix. Mechanical properties results show that the strength and elongation are both improved after hot extrusion.