Studies on thermoelectric figure of merit of Na-doped p-type polycrystalline SnSe

作者：Chere Eyob K^*; Zhang Qian; Dahal Keshab; Cao Feng; Mao Jun; Ren Zhifeng

来源：Journal of Materials Chemistry A, 2016, 4(5): 1848-1854.

DOI：10.1039/c5ta08847j

• Electrical conductivity
• Hot-pressing direction
• Na doped
• Na doping
• P-type
• Polycrystalline
• Power factors
• Thermoelectric figure of merit

SnSe has attracted some attention due to the recent report of record high thermoelectric figure-of-merit (ZT) of similar to 2.6 at about 923 K in single crystals. Even though the ZT is high in single crystal SnSe, it was very low in its polycrystalline form due to the very low electrical conductivity (<10(3) S m(-1)) from 300 K to 700 K. In this work, we report studies on enhancement of electrical conductivity by Na doping to optimize the carrier concentration in polycrystalline SnSe prepared by melting and hot pressing. A room temperature carrier concentration of similar to 2.7 x 10(19) cm(-3) was obtained in 2 atm% Na-doped SnSe samples with the highest power factor obtained in 1.5 atm% Na-doping. A peak ZT of similar to 0.8 was achieved at 773 K along the hot pressing direction and the average ZT was improved.

• 出版日期2016