Aqueous colloidal processing of near-net shape B4C-Ni cermet compacts

作者：Rodriguez Rojas Fernando; Moreno Rodrigo; Guiberteau Fernando; Ortiz Angel L^*

来源：Journal of the European Ceramic Society, 2016, 36(8): 1915-1921.

DOI：10.1016/j.jeurceramsoc.2016.02.051

• B4C
• Colloidal processing
• Cermets
• Near-net shaping

Aqueous colloidal processing was optimized for the environmentally friendly preparation of concentrated suspensions (29-40 vol.% solids loadings) suitable for the near-net shaping of B4C + 16.6 vol.%Ni cermet compacts by slip casting. Specifically, on the basis of studies with dilute suspensions, it was confirmed that using very basic pHs (i.e., 10) is the key to ensuring the inertness and dispersibility of the Ni particles in water, and that deflocculant contents of at least similar to 0.5 wt.% PIN and PAA are required to promote the colloidal stability of the B4C and Ni particles, respectively. Concentrated B4C + 16.6 vol.%Ni suspensions were consequently prepared at pH 11 with 1 wt.% PIN and PAA, and it was found that sonication for 1 min optimizes the rheological properties. Lastly, these concentrated suspensions were proven to be suitable for the slip casting of robust, highly-dense B4C-Ni cermet compacts with near-net shape, whose green microstructures are very uniform, exhibit well-dispersed and packed particles, with no evidence of cracks or macrodefects, and with relative densities greater than 58% of the theoretical.

• 出版日期2016-7