NiO Nanocrystalline/Reduced Graphene Oxide Composite Film with Enhanced Electrochromic Properties

作者：Lang, Fengpei^*; Liu, Jingbing; Wang, Hao; Yan, Hui

来源：Nano, 2017, 12(5): 1750058.

DOI：10.1142/S1793292017500588

• NiO
• electrochromic
• graphene
• composite film

The NiO nanocrystalline/reduced graphene oxide (rGO) composite film was successfully synthesized using a simple hot-injection and dip coating method. The as-prepared samples were characterized using X-ray diffraction (XRD), Raman, scanning electron microscope (SEM), ultraviolet and visible spectrophotometer (UV). Compared to the NiO film, the NiO nanocrystalline/rGO composite film exhibits enhanced electrochromic properties and large Delta T (40.7% at 550 nm), fast switching speed (t(c) = 4.3s and t(b) = 3.9s), high coloration efficiency (12.85 cm(2) C-1) and better cycling performance (1000 cycles). The improvement of the electrochromic properties was attributed to the large specific surface area and good conductivity of the rGO.

• 出版日期2017-5
• 单位北京工业大学