Multifunctional polymers with biomimetic compound architectures via nanoporous AAO films for efficient solar energy harvesting in dye-sensitized solar cells

作者：Dudem Bhaskar; Leem Jung Woo; Lim Joo Ho; Lee Soo Hyun; Yu Jae Su^*

来源：RSC Advances, 2015, 5(109): 90103-90110.

DOI：10.1039/c5ra16276a

We report the considerable enhancement of the solar power conversion efficiency (PCE) in dye-sensitized solar cells (DSSCs) using polydimethylsiloxane (PDMS) patterned with a novel biomimetic compound architecture (CA) (i.e., hierarchical nanobumps/microcone arrays) with light-harvesting and self-cleaning functions as a protective cover-layer. The CA-PDMS is transferred from a nanoporous anodic alumina oxide mold by a facile and cost-effective soft imprint lithography via a microcone-patterned sapphire substrate. A lamination of CA-PDMS on the glass leads to increased total and diffuse transmittance properties (i.e., antireflection and light scattering effects), simultaneously, compared to bare glass over a wide wavelength range of 350-800 nm, exhibiting a much larger solar weighted total transmittance (T-SW) value of similar to 94% and an average haze ratio (H-A) value of similar to 49.7% (T-SW approximate to 90.4% and H-A approximate to 1.4% for bare glass). In addition, sand grains on the hydrophobic surface with a water contact angle of similar to 134 degrees are clearly washed by rolling down water droplets (i.e., self-cleaning effect). To simply demonstrate the device applicability, CA-PDMS is introduced onto an outer surface of the front glass substrate in a DSSC. The resulting DSSC with CA-PDMS exhibits a boosted PCE value of similar to 8.24% mainly due to a strongly increased short-circuit current density (J(SC)) value of similar to 18.11 mA cm(-2) compared to the reference DSSC with bare glass (PCE approximate to 7.45% and J(SC) approximate to 16.37 mA cm(-2)) under AM1.5G illumination, indicating a large PCE enhancement percentage value of similar to 10.7%.

• 出版日期2015