Stable Wollastonite-Cuspidine Glass-Ceramic Using Inexpensive Raw Materials

作者：Al Harbi Omar A; Hamzawy Esmat M A^*

来源：Silicon, 2014, 6(4): 257-264.

DOI：10.1007/s12633-014-9241-z

• Silicate glasses
• Crystallization
• Differential thermal analysis
• Dilatometery

Transparent glasses within the K2O-CaO-SiO2-F composition were prepared. The influence of CaF2, TiO2, Li2O, Li2O-TiO2 and CeO2 additions on the crystallization of the parent glass has been investigated. Crystallization process gave wollastonite and cuspidine as the major phases whereas; xontolite and traces of miserite were developed as subordinate ones. Wollastonite was developed alone in the temperature range of 800 A degrees C-1100 A degrees C in Li2O-containing the base glass. Wollastonite and cuspidine were stable in the 800-1100 A degrees C range in Li2O+TiO2-containing samples and within the 900 A degrees C-1100 A degrees C range in CaF2 and CeO2 containing samples. The microstructure of the Li2O-containing glass-ceramic showed an interlocked needle in nano-scale wollastonite crystals, while fibrous textures were developed in all other crystallized samples at 1000 A degrees C. The thermal expansion coefficient value of the crystallized samples was between 7.596 to 8.708 X10 (-6) A degrees C-1 (20-500 A degrees C) and the higher values reflect the increase of crystallization content of cuspidine and even the traces of miserite. This glass-ceramic is thought to be important in dental laboratories.

• 出版日期2014-10