Mixed ionic-electronic conductivity and thermochemical expansion of Ca and Mo co-substituted pyrochlore-type Gd2Ti2O7

作者：Zakharchuk Kiryl; Kravchenko Ekaterina; Fagg Duncan P; Frade Jorge R; Yaremchenko Aleksey A^*

来源：RSC Advances, 2016, 6(74): 70186-70196.

DOI：10.1039/c6ra14600g

Phase relationships, transport properties and thermomechanical behavior of acceptor- and donor-co-substituted Gd2Ti2O7 were studied for possible application in solid oxide fuel cell anodes. The range of (Gd1-xCax)(2)(Ti1-yMoy)(2)O7-delta solid solutions with a cubic pyrochlore-type structure was found to be limited to 0.10 < x < 0.15 and 0.05 < y < 0.10 under oxidizing conditions. No evidence of phase instability of substituted materials was detected in the course of the electrical and thermogravimetric studies down to oxygen partial pressures as low as 10(-19) atm at 950 degrees C. (Gd1-xCax)(2)(Ti1-yMoy)(2)O7-delta ceramics possess moderate thermal expansion coefficients compatible with solid electrolytes, (10.5-10.7) x 10(-6) K-1 at 25-1100 degrees C in air, and demonstrate remarkable dimensional stability with nearly zero chemical expansion down to p(O-2) x 10(-1)2 atm at 950 degrees C. Though co-substitution by Mo suppresses oxygen-ionic conduction under oxidizing conditions, reducing oxygen partial pressure increases both ionic and n-type electronic transport. (Gd1-xCax)(2)(Ti0.95Mo0.05)(2)O7-delta (x = 0.07-0.10) pyrochlores are mixed conductors under SOFC anode operation conditions, but comparatively low total conductivity limits its applicability as electrode materials.

• 出版日期2016