Mechanism growth of multiwalled carbon nanotubes on carbon black

作者：Donnet Jean Bapstiste; Oulanti Hanae; Le Huu Thang^*

来源：Diamond and Related Materials, 2008, 17(7-10): 1506-1512.

DOI：10.1016/j.diamond.2008.01.001

• nanotubes
• combustion synthesis
• nanoparticles

The growth of multiwalled carbon nanotubes (MWCNTs) on carbon black has been studied using a combustion oxygen/acetylene flame method. Different types of carbon black and reaction temperatures were evaluated for the growth of carbon nanotubes. The reaction was stopped after different short duration times of deposition in an attempt to observe the growth of carbon nanotubes. The samples were characterized by Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM) and by Raman Spectroscopy. We have observed the transformation of the carbon black surface into graphitic sheets and the start formation of tubes from these graphitic sheets. The length of the tubes is increased but the diameter is decreased with increased deposition times. Carbon nanotubes with 10-20 nm of diameter and a length of about 50 mu m are obtained after 1 min deposition. The growth of multiwalled carbon nanotubes on carbon black is a phenomenon that can not be fully explained by carbon nanotubes growth models currently known. Our results lead its to propose a mechanism for the solid-state transformation of the carbon black particles surface into nanotubes in the oxygen/acetylene flame.

• 出版日期2008-10