Ab initio study of Ga-GaN system: Transition from adsorbed metal atoms to a metal-semiconductor junction

作者：Witczak Przemyslaw^*; Kempisty Pawel; Strak Pawel; Krukowski Stanislaw

来源：Journal of Vacuum Science and Technology A: Vacuum, Surfaces and Films , 2015, 33(6): 061101.

DOI：10.1116/1.4927166

Ab initio studies of a GaN(0001)-Ga system with various thicknesses of a metallic Ga layer were undertaken. The studied systems extend from a GaN(0001) surface with a fractional coverage of gallium atoms to a Ga-GaN metal-semiconductor (m-s) contact. Electronic properties of the system are simulated using density functional theory calculations for different doping of the bulk semiconductor. It is shown that during transition from a bare GaN(0001) surface to a m-s heterostructure, the Fermi level stays pinned at a Ga-broken bond highly dispersive surface state to Ga-Ga states at the m-s interface. Adsorption of gallium leads to an energy gain of about 4 eV for a clean GaN(0001) surface and the energy decreases to 3.2 eV for a thickly Ga-covered surface. The transition to the m-s interface is observed. For a thick Ga overlayer such interface corresponds to a Schottky contact with a barrier equal to 0.9 and 0.6 eV for n- and p-type, respectively. Bond polarization-related dipole layer occurring due to an electron transfer to the metal leads to a potential energy jump of 1.5 eV, independent on the semiconductor doping. Additionally high electron density in the Ga-Ga bond region leads to an energy barrier about 1.2 eV high and 4 angstrom wide. This feature may adversely affect the conductivity of the n-type m-s system.

• 出版日期2015-11