A structural investigation relating to the pozzolanic activity of rice husk ashes

作者：Nair Deepa G^*; Fraaij Alex; Klaassen Adri A K; Kentgens Arno P M

来源：Cement and Concrete Research, 2008, 38(6): 861-869.

DOI：10.1016/j.cemconres.2007.10.004

• rice husk ash
• silica
• pozzolanas
• cement
• Si-29 MAS NMR
• XRD

Various factors determine the applicability of rice husk ash (RHA) as a pozzolanic material. The amount and accessibility of reactive sites is thought to be a key factor. A structural study of RHA samples in relation to their reactivity has been performed; Silica in RHA formed by burning rice husk in a laboratory furnace under continuous supply of air have been characterized as a function of incineration temperature, time and cooling regime. The characterization methods included chemical analyses, conductivity measurements, microscopic analysis, X-ray diffraction (XRD) and Si-29 magic-angle spinning (MAS) nuclear magnetic resonance (NMR). In line with earlier observations, the analyses show that the highest amounts of amorphous silica occur in samples burnt in the range of 500 degrees C-700 degrees C. The Si-29 NMR data allow direct identification of the reactive silanol sites in the RHA samples. De-convolution of the NMR spectra clearly shows that the quickly cooled RHA resulting from burning rice husk for 12 h at 500 degrees C has the highest amount of silanol groups. This sample also induced the largest drop in conductivity when added to a saturated calcium hydroxide solution giving an indication of its reactivity towards lime. Therefore, this RHA is the favorable sample to be used as pozzolanic cement additive.

• 出版日期2008-6